Ketron™ SP HPV PEEK bearing grade is reinforced with carbon fiber, graphite and PTFE lubricants. With the lowest coefficient of friction and the best machinability for all PEEK grades, it is an excellent combination of low friction, low wear, high LPV, low mating part wear and easy machining. This makes it ideal for aggressive service bearings, bushings, rollers and thrust washers.
FASTIGHETER
wear-resistant
High limiting pressure velocity PV value
High mechanical strength and stiffness
Extremely low coefficient of friction
Excellent machinability
Termiska egenskaper
Fastighet
Värde
Värme Avböjningstemperatur vid 1,8 MPa (264 psi) (ºC)
195
Kontinuerlig tillåten driftstemperatur i luft
250
Mekaniska egenskaper
Fastighet
Värde
Draghållfasthet (MPa)
65
Elasticitetsmodul för drag (MPa)
5,950
Tryckspänning vid 1% nominell töjning (MPa)
46
Tryckspänning vid 2% nominell töjning (MPa)
80
Tryckspänning vid 5% nominell töjning (MPa)
120
Böjhållfasthet (MPa)
Charpy-slag i skåran (kJ/m²)
3
Kemiska egenskaper
Fastighet
Värde
Varmvatten / ånga
Syror, svaga
Syror, starka (pH 1-3)
Alkalier, svaga
Alkalier, starka (pH 11-14)
Kolväten - Aromatiska
Kolväten - alifatiska
Ketoner, estrar
Klorerade lösningsmedel
Alkoholer
Oorganiska saltlösningar
Elektriska egenskaper
Fastighet
Värde
Dielektrisk hållfasthet (kV/mm)
Egenskaper för certifiering
Fastighet
Värde
FDA
Uppfyller inte kraven
Europeiskt livsmedelsgodkännande
Uppfyller inte kraven
NSF
Uppfyller inte kraven
3A-SSI
Uppfyller inte kraven
Kanada AG
USDA
Uppfyller inte kraven
Brandfarlighet (UL-klassning)
V-0
Medicinsk användning
Diverse fastigheter
Fastighet
Värde
Basmaterial
PEEK
Varumärke Familj
Färger
Black
Densitet (g/cm3)
1.45
Vattenabsorption efter 24 timmars nedsänkning i vatten (%)