Ketron™ SP HPV PEEK bearing grade is reinforced with carbon fiber, graphite and PTFE lubricants. With the lowest coefficient of friction and the best machinability for all PEEK grades, it is an excellent combination of low friction, low wear, high LPV, low mating part wear and easy machining. This makes it ideal for aggressive service bearings, bushings, rollers and thrust washers.
EIGENSCHAPPEN
wear-resistant
High limiting pressure velocity PV value
High mechanical strength and stiffness
Extremely low coefficient of friction
Excellent machinability
Thermische eigenschappen
Eigendom
Waarde
Warmteafbuigingstemperatuur bij 1,8MPa (264 psi) (ºC)
195
Continu toelaatbare bedrijfstemperatuur in lucht
250
Mechanische eigenschappen
Eigendom
Waarde
Treksterkte (MPa)
65
Elasticiteitsmodulus (MPa)
5,950
Drukspanning bij 1% nominale rek (MPa)
46
Drukspanning bij 2% nominale rek (MPa)
80
Drukspanning bij 5% nominale rek (MPa)
120
Buigsterkte (MPa)
Charpy Ingeslagen Impact (kJ/m²)
3
Chemische eigenschappen
Eigendom
Waarde
Heet water / stoom
Zuren, Zwak
Zuren, sterk (pH 1-3)
Alkaliën, Zwak
Alkaliën, sterk (pH 11-14)
Koolwaterstoffen - Aromatische
Koolwaterstoffen - Alifatische
Ketonen, Esters
Gechloreerde oplosmiddelen
Alcoholen
Anorganische zoutoplossingen
Elektrische eigenschappen
Eigendom
Waarde
Diëlektrische sterkte (kV/mm)
Certificeringseigenschappen
Eigendom
Waarde
FDA
Niet in overeenstemming
Europese voedselgoedkeuring
Niet in overeenstemming
NSF
Niet in overeenstemming
3A-SSI
Niet in overeenstemming
Canada AG
USDA
Niet in overeenstemming
Ontvlambaarheid (UL-classificatie)
V-0
Medisch gebruik
Diverse eigenschappen
Eigendom
Waarde
Basismateriaal
PEEK
Merk Familie
Kleuren
Zwart
Dichtheid (g/cm3)
1.45
Waterabsorptie na 24 uur onderdompeling in water (%)