Semitron® CNT Polyoxymethylene POM-C is an extruded carbon nano tube-filled grade, developed specifically for electronic fixture applications that require a precise surface resistivity range, yet offer increased dimensional stability versus conventional POM ESd products. In addition to these properties, Semitron® CNT POM-C also offers superior stiffness and strength, while also maintaining an extremely low moisture absorption rate of 0.25% at 24 hour, and 0.75% at saturation. This grade in particular can be found throughout the semiconductor and electronics industry as integrated chip test jigs, test sockets, PCB test jigs, and in basic electronics assembly fixturing applications.

EIGENSCHAPPEN

---

• Developed specifically for electronic fixture applications that require a precise surface resistivity range
• Increased dimensional stability
• Superior stiffness and strength
• Low moisture absorption rate of 0.25% at 24 hour, and 0.75% at saturation
• Best utilized in the semiconductor and electronics industry

Thermische eigenschappen

Eigendom	Waarde
Warmteafbuigingstemperatuur bij 1,8MPa (264 psi) (ºC)
Continu toelaatbare bedrijfstemperatuur in lucht

---

Mechanische eigenschappen

Eigendom	Waarde
Treksterkte (MPa)
Elasticiteitsmodulus (MPa)
Drukspanning bij 1% nominale rek (MPa)
Drukspanning bij 2% nominale rek (MPa)
Drukspanning bij 5% nominale rek (MPa)
Buigsterkte (MPa)
Charpy Ingeslagen Impact (kJ/m²)

---

Chemische eigenschappen

Eigendom	Waarde
Heet water / stoom	Beperkt
Zuren, Zwak	Beperkt
Zuren, sterk (pH 1-3)
Alkaliën, Zwak	Aanvaardbaar
Alkaliën, sterk (pH 11-14)	Aanvaardbaar
Koolwaterstoffen - Aromatische	Not acceptable
Koolwaterstoffen - Alifatische
Ketonen, Esters
Gechloreerde oplosmiddelen
Alcoholen	Aanvaardbaar
Anorganische zoutoplossingen	Aanvaardbaar

---

Elektrische eigenschappen

Eigendom	Waarde
Diëlektrische sterkte (kV/mm)

---

Certificeringseigenschappen

Eigendom	Waarde
FDA	Niet in overeenstemming
Europese voedselgoedkeuring	Niet in overeenstemming
NSF	Niet in overeenstemming
3A-SSI	Niet in overeenstemming
Canada AG
USDA	Niet in overeenstemming
Ontvlambaarheid (UL-classificatie)	HB
Medisch gebruik

---

Diverse eigenschappen

Eigendom	Waarde
Basismateriaal	POM-C
Merk Familie
Kleuren	Black
Dichtheid (g/cm3)
Waterabsorptie na 24 uur onderdompeling in water (%)
Waterabsorptie bij verzadiging in water (%)
Slijtagefactor (µm/km)
Beschikbare vormen	Plate Rod
Hoofdgebruik Dragend en/of structureel	Bearing Structural